If a PLA or PETG mask cracks, especially when printed as a light weight/thin wall, it will cut your face like a knife. It may not be happen on the first day, but it will happen one day, maybe while you are talking, and it will be sudden. Thin walled...

I keep using PLA & the predefined “0.25mm DRAFT” print setting with 20% infill and no supports on my Průša MINI and it works just fine.One advice though - do not screw the screws too tightly especially when using the Cylindric_head parameter...

If a PLA or PETG mask cracks, especially when printed as a light weight/thin wall, it will cut your face like a knife. It may not be happen on the first day, but it will happen one day, maybe while you are talking, and it will be sudden. Thin walled...

The diameter of the tube is such that the coupling can form its own threads without cracking the tube. feed the PTFE tube through the coupling, ensuring that it goes several mm past the coupling until it seats into position, as shown in the dimension...

When I went to a 6-Cell it cracked at the motor mount with PLA+ but has held up fine with PTEG and has over 30 runs on it. This is modeled after a P9 RC Rigger (Outrigger) Racing Boat. Turn fin is critical on this boat. Designed to take 7.8MM arrows...

Don't overtension the screws, especially if you go with the acrylic faceplate that I bought, or you could crack things (I did). The bracket side should be more resilient, and also matters more since you're trying to get a better seal there. The...

Seriously, I can't stress this enough, I had cleaned and cured everything, had it laid down but once I turned it upright, after a few days I noticed resin had leaked all over it, I had to reprint the entire bottom half as it all started cracking. I...

You can enable the fan on ABS prints to improve quality, but this will greatly increase the risk of warping and cracking. Enabling the fan continuously with ABS is only feasible in the following cases: * for small objects printed with thin layers. A...

...I tested the original design with CarbonFill Black and Nylon CF, both cracked from the same area. - Added 12mm wheel hexes. - Added front hinge pin plate 38mm. - Added front hinge pin plate 40mm. - Added front hinge pin plate shim 0,5mm.

You can enable them in Main parameters section, and adjust them for your particular needs in Mounting pads section.One advice though - do not screw the screws too tightly to the pads especially when using the Has conic head parameter - the...

Just push it all in and crack the support loose toward the middle. Do the same on the other side. Now most of the support should be loose an can be removed with some pliers. In the end stick the scissors in and open them. If you hear support...

Tighten the handles firmly but be careful not to over-tighten or parts may crack. IMPORTANT! : Before inserting the bit-holders into the wheels, insert a 1/8" (3mm) tool bit into each opening. The reason for this is that there is likely to be some...

It might click and crack a little. Don't worry, they won't get damaged.</li><li>For disassembly, press down on one cup and press up on the other until they separate. Sometimes wiggeling or slight twisting helps (No, I'm not talking about dancing but...

If a PLA or PETG mask cracks, especially when printed as a light weight/thin wall, it will cut your face like a knife. It may not be happen on the first day, but it will happen one day, maybe while you are talking, and it will be sudden. Thin walled...

The big thing here is you want to form a waterproof seal so the water only runs through the spout and not outside through the cracks.  Pump and Mister PlacementThe pump is placed in the main basin and the mister is placed in the bottom...

Just make sure that they are flat and even when the glue sets.The glue is just to hold them together whilst wrapping them in felt, so it's not structuraly important.In fact, since they are so thin and the contact area is so small the glue is bound to...

The design relies on the inherent flexibility and tendency to creep of PET G rather than crack like PLA over time. Hence can tolerate distributed elastic loads well if printed in continuous looped wallls in the direction of the force applied. ...

[UPDATE] I have managed to crack one of the moulds during clamping. It can be repaired with glue and didn't interfere with its ability to form a board, but between that and the dents left in the mould by the clamping process, I would suggest...

If a PLA or PETG mask cracks, especially when printed as a light weight/thin wall, it will cut your face like a knife. It may not be happen on the first day, but it will happen one day, maybe while you are talking, and it will be sudden. Thin walled...

It's easy to break or crack the little fingers. Slide the right wheel and axle through the right_bevel_gear assembly. The bevel gear should spin freely on the axle without a lot of wobble. Then slide the right ratchet onto the axle. Next is the...

I can't guarantee I will be able to make requested changes of course, but if I have the time and can see a way, I may take another crack at it. Thanks for checking it out!</p> <h3>Print Settings</h3> </li> </ul> <p><strong>Notes:</strong></p>...

One daughter was touched by the mist and her skin started to crack and crumble like charred bark on a burned piece of wood. As the daughter was screaming in pain and the others screaming in panic, Arastacia stood there in shock, never has she seen...

Not necersarilly in that order and would recommend loosely fastening them then tightening them all last but not too much to deform or crack anything. 28. Re-assemble the Pint as usual and take it for a spin. ...I suggest keeping an eye on the...

To reduce the risk of cracking and ruining your new part, use one of them as you would a thread tap, by carefully driving it part way in, removing it, clearing any debris, and repeating, lining it up with the threads' cuts each time. ... You can now...

Dremel Pillar Drill (Drill Press)&nbsp;Precision pillar drill stand for a Dremel giving a plunge depth of about 70 mm.&nbsp; Any Dremel that has the ‘standard’ 16 mm screw at the business end should fit but I’ve only tested this with the Model...

(Silky PLA is always a PLA blend, usually a mystery blend, and should never be considered food safe-ISH unless stated otherwise.) I say "safe-ish" because filaments are rarely certified for food use, but you may be able to find info stating 'as far...

It might click and crack a little. Don't worry, they won't get damaged.</li><li>For disassembly, press down on one cup and press up on the other until they separate. Sometimes wiggeling or slight twisting helps (No, I'm not talking about dancing but...

... 0.032" seems to crack my carriages with fair regularity, while 0.020" doesn't have sufficient power (although it may be useful for shrinking the game to a smaller footprint). McMaster-Carr item number 9074K33 is a 10-foot length of 0.025" steel. 3.

It's easy to break or crack the little fingers. Slide the right wheel and axle through the right_bevel_gear assembly. The bevel gear should spin freely on the axle without a lot of wobble. Then slide the right ratchet onto the axle. Next is the left...

 I have since uploaded them in the folder named “Latch Parts”.Update 12/25/2023 - Thanks to feedback from Stephen Friend, who advised me that the handle was missing, I've added that part to the “BOTTOM PARTS” folder.UPDATE 1/20/2024: Thanks to some...